S-Plastic Stat-kon EE005 a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material i

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon EE005 a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material i

Name: SPlastic Statkon EE005 a compound based on Polyetherimide resin containing Carbon Fiber Added features of this material i
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon EE005 a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material i wholesale

Brand Name : S-Plastic Stat-kon

Model Number : EE005

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon EE005 resin is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	200	MPa	ASTM D 638
Tensile Strain, break	2.1	%	ASTM D 638
Tensile Modulus, 50 mm/min	12330	MPa	ASTM D 638
Flexural Stress	277	MPa	ASTM D 790
Flexural Modulus	14320	MPa	ASTM D 790
Tensile Stress, break	194	MPa	ISO 527
Tensile Strain, break	2.1	%	ISO 527
Tensile Modulus, 1 mm/min	11700	MPa	ISO 527
Flexural Stress	246	MPa	ISO 178
Flexural Modulus	15010	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	448	J/m	ASTM D 4812
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	10	J	ASTM D 3763
Multiaxial Impact	7	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	29	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	207	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.9E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	2.71E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.92E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	2.71E-05	1/°C	ISO 11359-2
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	206	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.365	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.16	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.3 - 0.5	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.3 - 0.5	%	ISO 294
Density	1.36	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.23	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+02 - 1.E+06	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+02 - 1.E+05	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4	hrs
Maximum Moisture Content	0.05	%
Melt Temperature	360 - 365	°C
Front - Zone 3 Temperature	365 - 375	°C
Middle - Zone 2 Temperature	355 - 365	°C
Rear - Zone 1 Temperature	345 - 355	°C
Mold Temperature	120 - 150	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm
Source GMD, last updated:10/01/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon EE005.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!