S-Plastic Stat-kon EX07311P an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon EX07311P an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for

Name: SPlastic Statkon EX07311P an easy flowing ESDsafe compound based on Polyetherimide resin This compound is developed for
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon EX07311P an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for wholesale

Brand Name : S-Plastic Stat-kon

Model Number : EX07311P

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 345°C/10.0 kg : 30

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon EX07311P resin is an easy flowing ESD-safe compound based on Polyetherimide resin. This compound is developed for good dimensional stability for use in ESD Tray for Backend Semicon and HDD tray applications.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	175	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.1	%	ASTM D 638
Tensile Modulus, 5 mm/min	15000	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	200	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	11500	MPa	ASTM D 790
Tensile Stress, break, 5 mm/min	174	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.9	%	ISO 527
Tensile Modulus, 1 mm/min	15200	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	203	MPa	ISO 178
Flexural Strain, break, 2 mm/min	1.7	%	ISO 178
Flexural Modulus, 2 mm/min	13200	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	56	J/m	ASTM D 256
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	202	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.9E-06	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.38E-05	1/°C	ASTM E 831
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	204	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.56	g/cm³	ASTM D 792
Mold Shrinkage, flow	0.29	%	S-Plastics Method
Mold Shrinkage, xflow	0.36	%	S-Plastics Method
Wear Factor Washer	20	10^-10 in^5-min/ft-lb-hr	ASTM D 3702 Modified
Dynamic COF	0.4	-	ASTM D 3702 Modified
Density	1.56	g/cm³	ISO 1183
Melt Volume Rate, MVR at 345°C/10.0 kg	30	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+05 - 1.E+06	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+05 - 1.E+06	Ohm	ASTM D 257
Surface Resistivity, ROA	1.E+05 - 1.E+06	Ohm	IEC 60093
Source GMD, last updated:07/23/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	350 - 400	°C
Nozzle Temperature	345 - 400	°C
Front - Zone 3 Temperature	345 - 400	°C
Middle - Zone 2 Temperature	340 - 400	°C
Rear - Zone 1 Temperature	330 - 400	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:07/23/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon EX07311P.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!