S-Plastic Stat-kon EX08308C a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications

Name: SPlastic Statkon EX08308C a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon EX08308C a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications wholesale

Brand Name : S-Plastic Stat-kon

Model Number : EX08308C

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94V-0 Flame Class Rating (3) : 0.4

Contact Now

S-Plastics Stat-kon EX08308C resin is a high cleanliness Polyetherimide Compound reinforced with Carbon Fiber for use in applications requiring the highest level of cleanliness. This compound is compounded using LNP CCS Technology.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, brk, Type I, 5 mm/min	188	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	21090	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	209	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	16000	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	309	J/m	ASTM D 4812
Izod Impact, notched, 23°C	50	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	5	J	ASTM D 3763
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 6.4 mm, unannealed	190	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.83E+00	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.95E+00	1/°C	ASTM E 831
PHYSICAL	Value	Unit	Standard
Density	1.387	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.18	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.25 - 0.31	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.36 - 0.42	%	ASTM D 955
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	2.51E+04 - 2.51E+05	Ohm-cm	ASTM D 257
Surface Resistivity	4.5E+03 - 9.E+04	Ohm	ASTM D 257
Static Decay, 5000V to <50V	0.1	< seconds	FTMS101B
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.4	mm	UL 94
Source GMD, last updated:12/31/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	370 - 410	°C
Nozzle Temperature	350 - 405	°C
Front - Zone 3 Temperature	360 - 415	°C
Middle - Zone 2 Temperature	350 - 405	°C
Rear - Zone 1 Temperature	340 - 395	°C
Hopper Temperature	80 - 120	°C
Mold Temperature	140 - 180	°C
Source GMD, last updated:12/31/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon EX08308C.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!