S-Plastic Stat-kon DX09301C Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconducto

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon DX09301C Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconducto

Name: SPlastic Statkon DX09301C Low Ionic Low Outgassing Low LPC and ESD safe Polycarbonate compound suitable for Semiconducto
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon DX09301C Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconducto wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DX09301C

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon DX09301C resin is Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application.Added features of this material include: Clean Compounding System.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	64	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	51	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	5.4	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	15	%	ASTM D 638
Tensile Modulus, 50 mm/min	2670	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	101	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2600	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	66	MPa	ISO 527
Tensile Stress, break, 5 mm/min	54	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	3.1	%	ISO 527
Tensile Strain, break, 5 mm/min	12	%	ISO 527
Tensile Modulus, 1 mm/min	2600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	99	MPa	ISO 178
Flexural Modulus, 2 mm/min	2560	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	2160	J/m	ASTM D 4812
Izod Impact, notched, 23°C	52	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	8	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	200	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	4	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	138	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	137	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.224	g/cm³	ASTM D 792
Mold Shrinkage, flow, 24 hrs (5)	0.5 - 0.7	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.5 - 0.7	%	ASTM D 955
Density	1.22	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+05 - 1.E+08	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+05 - 1.E+08	Ohm	ASTM D 257
Static Decay, 5000V to <50V	0.1	< seconds	FTMS101B
Source GMD, last updated:2010/05/21

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	305 - 325	°C
Front - Zone 3 Temperature	320 - 330	°C
Middle - Zone 2 Temperature	310 - 320	°C
Rear - Zone 1 Temperature	295 - 305	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2010/05/21

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DX09301C.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!