S-Plastic Stat-kon DEL13EXC a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this ma

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon DEL13EXC a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this ma

Name: SPlastic Statkon DEL13EXC a compound based on Polycarbonate resin containing Carbon Fiber PTFE Added features of this ma
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon DEL13EXC a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this ma wholesale

Brand Name : S-Plastic Stat-kon

Model Number : DEL13EXC

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon DEL13EXC resin is a compound based on Polycarbonate resin containing Carbon Fiber, PTFE. Added features of this
material include: Easy Molding.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	133	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	131	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	131	MPa	ASTM D 638
Tensile Strain, break	3	%	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D 638
Tensile Modulus, 50 mm/min	13400	MPa	ASTM D 638
Flexural Stress	199	MPa	ASTM D 790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	163	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	163	MPa	ASTM D 790
Flexural Modulus	9380	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	6520	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	126	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	1.3	%	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	13010	MPa	ISO 527
Flexural Stress	177	MPa	ISO 178
Flexural Modulus, 2 mm/min	10230	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	422	J/m	ASTM D 4812
Izod Impact, notched, 23°C	70	J/m	ASTM D 256
Multiaxial Impact	3	J	ISO 6603
Instrumented Impact Total Energy, 23°C	9	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	24	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	140	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	137	°C	ASTM D 648
CTE, -30°C to 30°C, flow	1.E-06	1/°C	ASTM D 696
CTE, -30°C to 30°C, xflow	7.E-06	1/°C	ASTM D 696
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	141	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	138	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.29	-	ASTM D 792
Density	1.28	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.11	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.6	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	0.08 - 0.1	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.18	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+00 - 3.E+00	Ohm	ASTM D 257
Source GMD, last updated:04/26/2005

Processing

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon DEL13EXC.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!