Home > LNP Stat Kon >

S-Plastic Stat-kon RFD02 a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this ma

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon RFD02 a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this ma

Name: SPlastic Statkon RFD02 a compound based on Nylon 66 resin containing Glass Fiber Carbon Powder Added features of this ma
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon RFD02 a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this ma wholesale

Brand Name : S-Plastic Stat-kon

Model Number : RFD02

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon RFD02 resin is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Powder. Added features of this material
include: Electrically Conductive.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	77	MPa	ASTM D 638
Tensile Strain, break	5.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	8270	MPa	ASTM D 638
Flexural Stress	131	MPa	ASTM D 790
Flexural Modulus	5510	MPa	ASTM D 790
Tensile Stress, break	74	MPa	ISO 527
Tensile Strain, break	5.1	%	ISO 527
Tensile Modulus, 1 mm/min	7400	MPa	ISO 527
Flexural Stress	139	MPa	ISO 178
Flexural Modulus	6300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	213	J/m	ASTM D 4812
Izod Impact, notched, 23°C	37	J/m	ASTM D 256
Izod Impact, unnotched 80104 +23°C	14	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	3	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	252	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	236	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.84E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.68E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	6.9E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.8E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	256	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	239	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.3	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.5	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	1 - 1.2	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	1.4 - 1.6	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	1.1	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5	%	ISO 294
Density	1.3	g/cm³	ISO 1183
ELECTRICAL	Value	Unit	Standard
Surface Resistivity	1.E+02 - 1.E+05	Ohm	ASTM D 257
Source GMD, last updated:09/24/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:09/24/2008

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon RFD02.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!