S-Plastic Stat-kon FX97333 a compound based on Polyethylene resin containing Carbon Powder. Added features of this material

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Stat-kon FX97333 a compound based on Polyethylene resin containing Carbon Powder. Added features of this material

Name: SPlastic Statkon FX97333 a compound based on Polyethylene resin containing Carbon Powder Added features of this material
Brand: S-Plastic Stat-kon
Price: 1 USD

Best S-Plastic Stat-kon FX97333 a compound based on Polyethylene resin containing Carbon Powder. Added features of this material wholesale

Brand Name : S-Plastic Stat-kon

Model Number : FX97333

Certification : COA/ICP Test/Rohs/MSDS

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Stat-kon FX97333 resin is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include:

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yield	20	MPa	ASTM D 638
Tensile Stress, break	20	MPa	ASTM D 638
Tensile Strain, yield	17.6	%	ASTM D 638
Tensile Strain, break	98.2	%	ASTM D 638
Tensile Modulus, 50 mm/min	810	MPa	ASTM D 638
Flexural Stress	19	MPa	ASTM D 790
Flexural Modulus	630	MPa	ASTM D 790
Tensile Stress, yield	18	MPa	ISO 527
Tensile Stress, break	14	MPa	ISO 527
Tensile Strain, yield	19.6	%	ISO 527
Tensile Strain, break	71.2	%	ISO 527
Tensile Modulus, 1 mm/min	660	MPa	ISO 527
Flexural Stress	710	MPa	ISO 178
Flexural Modulus	20700	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D 4812
Izod Impact, notched, 23°C	90	J/m	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	30	J	ASTM D 3763
Multiaxial Impact	70	J	ISO 6603
Izod Impact, unnotched 80104 +23°C	96	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	11	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	44	°C	ASTM D 648
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	44	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	0.994	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.02	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs	2 - 4	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs	2 - 4	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs	2 - 4	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	2 - 4	%	ISO 294
Density	0.99	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.99	%	ISO 62
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+02 - 1.E+05	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+02 - 1.E+05	Ohm	ASTM D 257
Source GMD, last updated:10/01/2004

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	230	°C
Front - Zone 3 Temperature	220 - 230	°C
Middle - Zone 2 Temperature	210 - 220	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	40 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:10/01/2004

Other related products we recommend:

For more information please download the datesheet
	S-Plastics Stat-kon FX97333.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!